Modell Nr .: q005 Spezifikation: IEC-Norm HS-Code: 85 Warenzeichen: VILLE INDUSTRY Herkunft: Ningbo China
Produktdetails
Daten von Fiberglas Ring,

PROPERTIES	UNIT OF MEASURE	TYPICAL
*Color *Resin content ( weight % ) *Glass fiber content ( weight % ) *Composit density   *Circumferential tensile strength at 20°C  (NOL test )   *Temperature at which the residual of  Initial tensile strength is greater then 85%   *Fiber diretion thermal expansion coefficient (CTE)   *Thermomechanical analysis: Glass transition temperature (ASTM  E  1545-93 )	% % g/cm³   Mpa (PSI)     °C (°F)     1/K     °C (°F)	Light brown 16-23 84-77 2.10-2.20   800-1200 (116000-174000)     300°C (572°F)     8.50E-06     300-350°C (572-662°F)
NOTE: Mechanical NOL data vary within a range determined by resin content and the ratio diameted thickness of the ring .This ratio gives a flexural mode that will cocur during  test and test data can vary for each type of ring.

Daten von Fiberglas Ring,

PROPERTIES	UNIT OF MEASURE	TYPICAL
*Color *Resin content ( weight % ) *Glass fiber content ( weight % ) *Composit density   *Circumferential tensile strength at 20°C  (NOL test )   *Temperature at which the residual of  Initial tensile strength is greater then 75%   *Fiber diretion thermal expansion coefficient (CTE)   *Thermomechanical analysis: Glass transition temperature (ASTM  E  1545-93 )	% % g/cm³   Mpa (PSI)     °C (°F)     1/K     °C (°F)	Light brown 16-23 84-77 2.10-2.20   800-1200 (116000-174000)     200°C (392°F)     8.50E-06     240-260°C (464-500°F)
NOTE: Mechanical NOL data vary within a range determined by resin content and the ratio diameted thickness of the ring .This ratio gives a flexural mode that will cocur during  test and test data can vary for each type of ring.